MACRKYD F-4038 70%
Download Technical Data Sheet
Short Oil, Penta Erithritol esterified Alkyd Resin modi, with Soya Fatty Acid
PRINCIPAL PROPERTIES
Excellent resistance to yellowing in light and heat, even at high temperatures in baking enamels very high gloss and very good gloss retention, excellent hardness and flexibility. Good adhesion steel, very good chemical resistance. In air drying application dries very fast.APPLICATION
White and light colored high quality baking enamels for motor cars, washing machines, refrigerators and kitchen equipment. Air drying systems with excellent build and color retention. Two component polyurethane lacquers. Automotive paints in air drying car refinish paints. Infinitely soluble in MTO/LAWS- AUTO REFINISH
- AIR DRYING
COMPOSITION
| Phthalic anhydride | Approx. 43 % |
| Fatty Acids | Approx. 38 % |
| Type of Fatty Acid | Soya Fatty Acid |
PHYSICAL CONSTANTS
| Viscosity in 50% Solution in O-Xylene at 30°C Temperature in Ford Cup B-4 | 100 – 125 Second |
| Acid Value (mg KOH/gm) | 15 Max |
| Color on Gardner Scale | 5 Max |
SOLUBILITY
| Xylene | Complete Soluble |
| n-Butyl Acetate | Complete Soluble |
| Methyl Ethyl Ketone | Complete Soluble |
| Turpentine | Complete Soluble |
| MTO /LAWS | Complete Soluble |
| n-Butanol | Limited soluble |
COMPATIBILITY
| MRGLY | Compatible |
| Long Oil in MTO/LAWS | Compatible |
| MF – 970 | Compatible |
| MF – 268/910 | Limited Compatible |
| D – 2040M | Not Compatible |
| C - 1030/1032 | Not Compatible |
| UF – 8/9001 | Not Compatible |
DELIVERY FORM
| F – 4038 | 70 ± 2% in Xylene |
Guideline for Baking Clear
| F – 4038 | 56.302 Gm |
| Mix Drier | 1.478 Gm |
| Toluene/Xylene | 42.22 Gm |
| Total | 100.00 Gm |
Suggested Mix Drier
| Calcium Octate (6%) | 10.00 Gm |
| Cobalt Octate (12%) | 2.833 Gm |
| Manganese Octate (6%) | 7.667 Gm |
| Lead Octate (36%) | 10.278 Gm |
| Xylene/Toluene | 8.112 Gm |
| Total | 38.890 Gm |
Drying Time
| Touch Dry | 17 Minutes Max |
| Tack Free | 260 Minutes Max |
| Hard Dry | 24 Hours |
| Panel Testing Over Night | H |