P-411 is high quality & extremely flexible linear polyester resin developed for Can coatings, sheet fed metal decorating and coil coatings applications.


  • Good substrate adhesion
  • Excellent flexibility
  • Good UV ink adhesion
  • Good exterior durability
  • Good exterior durability
  • Good film forming properties


P-411 is linear oil free polyester developed for use in Can Coatings, sheet fed Metal Decorating, coilcoatings and General Industrial applications.

P-411 is compatible with a wide range of melamine resins and is typically hexamethoxymethylmelamine and partially methylated melamine.

For an optimum performance with respect to level of cure, flexibility, hardness and impact resistance,a combination of P-411 with hexamethoxymethyl melamine resin at ratio of 70:30 to 85:15 on solidresin content is suggested.

To promote cure, the use of between1% to 5% of acid catalyst is recommended, e.g. paratoluenesulphonic acid, calculated on melamine solids.

Variation in the levels of P-411 and the type of amino resin will modify the overall performance ofthe coating. Increasing the level of amino resin (and catalyst) will generally tend to increase thehardness and solvent resistance of the coating but may compromise flexibility.

For Coil Coating:

Applications an 85:15 to 80:20 ratio, on solids, with hexamethoxymethyl melamine resin isrecommended with 2% PTSA catalyst on amino level.

For Metal Decorating:

On solids, of 72:18:10 OFPE: melamine: epoxy resin (epoxy equ. »500) with 2% PTSA solids amino issuitable.

Part methylated amino resin can be used in place of hexamethoxymethyl melamine and will developvery good hardness & solvent resistance but at the expense of flexibility.

General industrial enamels:

Can be formulated with 70:30 to 80:20 ratios with hexamethoxymethyl melamine or partmethylated melamine, with 2% PTSA catalyst


Viscosity as such in Brook Field RVT /S – 4, RPM – 12 at 25°C Temperature 80 – 120 Poise
Color on Gardner Scale 4 Max
Acid Value (mg KOH/gm) 10 Max
Hydroxyl Value 25 + 5
Solvent C - 10


n-Butyl Acetate Complete Soluble
Xylene Not Soluble
MTO /LAWS Not Soluble


P – 411 60 ± 2% in C – 10

Suggested Curing Schedules

Coil Coating 232°C - 240°C Temperature As per Requirement
Metal Decorating 160°C - 200°C Temperature 10 Minutes
General Industrial 150°C Temperature 30 Minutes
Request a Quote

PU Automotive Paint

If you are the type of person who can’t workout on an empty stomach, you may want to try this to boost your fat burn: Eat a meal made with “Slow Release” carbohydrates.


Paint for specific use

Sebastian Lagree’s Megaformer Machines put the Sweat in Pilates Mr.Lagree invented, the Megaformer,the basis of a core-burning workout.


Wood coating

Co-founders Lindsay and Moira Merrithew, along with a team of physical therapists sports medicine and fitness professionals,have spent over two decades refining the STOTT PILATES method of exercise


Alkyd air drying paint

POUND is a full-body cardio jam session, combining light resistance with constant simulated drumming.Each minute song is carefully calibrated with interval peaks and extended