MPA – 558
Solvent Less, reactive liquid type of Epoxy Hardener as Phenalkamine
MPA – 558 is low viscosity curing agent can be used for solvent free Epoxy Coating. Having excellent adhesion on unprepared metal surface and concrete substrate. Very fast curing agent, workable pot life having ability to resist moisture and can be used at low temperature.
Suitable for solvent free Epoxy Coating for Flooring and Pipe applications even under low temperature and damp application. Also can be used in contact with water.
|% Non Volatile||95% Above|
|Viscosity as such in Brook Field at 25°C Temperature||5 – 10 Poise|
|Color as such||17 Max|
|Amine Value mg KOH/gm||265 – 360|
|Hydrogen Equivalent Weight||95|
|Appearance||Amber Colored Liquid|
|Density as such at 25°C Temperature||0.98 ± 0.02|
|Recommended PHR (Liquid Epoxy Resin, EEW = 190)||50 – 65|
- Rapid cure, workable pot life at low temperature.
- Easy to mix.
- Excellent adhesion on unprepared surface and concrete surface.
- Excellent chemical resistance.
- Very good compatibility with other resins.
- Solvent free.
|MTO / WS / LAMS||Not Soluble|
|Epoxy – 450||Compatible|
|CR – 250||Compatible|
|MPA – 558||100% Liquid|
|CR – 250||100GRAMS||EPOXY – 450||100GRAMS|
|MPA – 558||50GRAMS||MPA – 558||22 – 26GRAMS|
PU Automotive Paint
If you are the type of person who can’t workout on an empty stomach, you may want to try this to boost your fat burn: Eat a meal made with “Slow Release” carbohydrates.
Paint for specific use
Sebastian Lagree’s Megaformer Machines put the Sweat in Pilates Mr.Lagree invented, the Megaformer,the basis of a core-burning workout.
Co-founders Lindsay and Moira Merrithew, along with a team of physical therapists sports medicine and fitness professionals,have spent over two decades refining the STOTT PILATES method of exercise
Alkyd air drying paint
POUND is a full-body cardio jam session, combining light resistance with constant simulated drumming.Each minute song is carefully calibrated with interval peaks and extended